AS2701高導熱矽膠 High Thermal Transfer
FEATURE(產品簡介)
- 10 : 1 VOLUMETERIC RATIO FOR MACHINE OR CARTRIDGE DISPENSING
- VERY FAST ROOM TEMP CURE
- THERMALLY CONDUCTIVE
- GOOD ADHESION TO MOST SUBSTRATES
DESCRIPTION(產品簡介)
SILCOTHERM 2 PART RTV SILICONE ADHESIVE SEALANT PASTE NON CORROSIVE FAST
參數表PARAMETERS
- CODE
AS2701
- FEATURE 1
10 : 1 volumeteric ratio for machine or cartridge dispensing
- FEATURE 2
Very fast room temp cure
- FEATURE 3
Thermally conductive
- FEATURE 4
Good adhesion to most substrates
- APPEARANCE
Thixotropic paste
- TEST CONDITIONS
After 7 days cure at 23°+/-2°C and 50+/-5% humidity
- COLOUR
Black
- COLOUR A PART
Grey
- COLOUR b PART
Black
- MIN WORKING TEMP - °C
-50°C
- MAX WORKING TEMP +°C
220 °C
- FDA
NO
- SHELF LIFE
6mths
- MIN STORAGE TEMPERATURE °C
-5 °C
- MAX STORAGE TEMPERATURE °C
+ 30°C
- PACK TYPE
2-PART
- MIX RATIO
10:1
- RHEOLOGY
Paste
- VISCOSITY A-PART MPAS
180000 mPas
- VISCOSITY B-PART MPAS
2800 mPas
- VISCOSITY MIXED PART MPAS
163000mPas
- NON CORROSIVE
YES
- CURE TYPE
Condensation
- RTV OR HEAT CURE
RTV
- SELF BONDING
Yes
- UL 94V-0
NO
- DURO SHORE A
64
- Tensile MPa
2.01MPa
- ELONGATION %
80 %
- EXTRUSION RATE G/MIN
124 g/min
- MODULUS YOUNGS MPA
6 MPa
- CTE VOLUMETRIC PPM/°C
372ppm/°C
- CTE LINEAR PPM/°C
124 ppm/°C
- TACK FREE TIME MINS
12mins
- MAX CURE MINS @ 25 °C
0.83hrs
- THERMAL CONDUCTIVITY W/MK
1.55 W/mK
- VOLUME RESISTIVITY OHMS CM
>1 2E+13 ohms cm
- DIELETRIC STRENGTH KV/MM
>18 kV/mm